Characterization and evaluation of rice husk ash and wood ash in sustainable clay matrix bricks
ترجمه فارسی عنوان
شناسایی و ارزیابی خاکستر پوسته برنج و خاکسترهای چوبی در آجرهای ماتریس پایدار
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
خاکستر پوسته برنج، خاکستر چوب، آجر خاک رس، پایداری، خواص فن آوری،
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
چکیده انگلیسی
The ash was characterized using particle size distribution analysis, chemical composition analysis by X-ray diffraction (XRD) and X-ray fluorescence (XRF), thermal analysis, elemental analysis, and scanning electron microscopy (SEM). Either rice husk ash or wood ash was used to replace different amounts (10-30 wt%) of clay in brick manufacture. Brick samples were formed by compression at 54.5 MPa and fired at temperatures of 900 or 1000 °C for 4 h, at a heating rate of 3 °C/min. The bricks' properties were compared to conventional products containing only clay and prepared following standard procedures. The bricks' technological properties depended on type and amount of ash used, and firing temperature. The results showed small variations due to firing temperature. Firing at 1000 °C achieved greater densification and thus lower water absorption and higher compressive strength firing at 900 °C produced higher porosity, which reduced compressive strength. Based on the results, 1000 °C was selected as the optimal firing temperature; and 10 wt% rice husk ash and 20 wt% wood ash as the optima amounts of biomass ash waste. Moreover, the bricks containing wood ash showed properties similar to the control bricks containing only clay and improved thermal conductivity. Finally, the bricks containing 10 wt% rice husk ash and 30 wt% wood ash fulfilled standard requirements for clay masonry units.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 43, Issue 1, Part A, January 2017, Pages 463-475
Journal: Ceramics International - Volume 43, Issue 1, Part A, January 2017, Pages 463-475
نویسندگان
D. Eliche-Quesada, M.A. Felipe-Sesé, J.A. López-Pérez, A. Infantes-Molina,