Low temperature preparation of CaCu3Ti4O12 ceramics with high permittivity and low dielectric loss
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Low temperature preparation of CaCu3Ti4O12 ceramics with high permittivity and low dielectric loss Low temperature preparation of CaCu3Ti4O12 ceramics with high permittivity and low dielectric loss](/preview/png/5438396.png)
چکیده انگلیسی
Low temperature preparation of CaCu3Ti4O12 ceramics with large permittivity is of practical interest for cofired multilayer ceramic capacitors. Although CaCu3Ti4O12 ceramics have been prepared at low temperatures as previously reported, they have rather low permittivity. This work demonstrates that CaCu3Ti4O12 ceramics can not only be prepared at low temperatures, but they also have large permittivity. Herein, CaCu3Ti4O12 ceramics were prepared by the solid state reaction method using B2O3 as the doping substance. It has been shown that B2O3 dopant can considerably lower the calcination and sintering temperatures to 870 °C and 920 °C, respectively. The relative permittivity of the low temperature prepared CaCu3Ti4âxBxO12 ceramics is about 5 times larger than the previously reported results in the literature. Furthermore, the dielectric loss of the CaCu3Ti4âxBxO12 ceramics is found to be as low as 0.03. This work provides a beneficial base for the future commercial applications of CaCu3Ti4O12 ceramics with large permittivity for the cofired multilayer ceramic capacitors.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 43, Issue 12, 15 August 2017, Pages 9178-9183
Journal: Ceramics International - Volume 43, Issue 12, 15 August 2017, Pages 9178-9183
نویسندگان
Yingyi Li, Wang Li, Guoping Du, Nan Chen,