Dynamic oxidation resistance and residual mechanical strength of ZrB2-CrSi2-SiC-Si/SiC coated C/C composites

To improve oxidation resistance of carbon/carbon (C/C) composites, a multiphase double-layer ZrB2-CrSi2-SiC-Si/SiC coating was prepared on the surface of C/C composites by pack cementation. Thermogravimetry analysis showed that the as-prepared coating could provide effective oxidative protection for C/C composites from room temperature to 1490 °C. After thermal cycling between 1500 °C and room temperature, the fracture behaviors of the as-prepared specimens changed and their residual flexural strengths decreased as thermal cycles increased. The specimen after 20 thermal cycles presented pseudo-plastic fracture characteristics and relatively high residual flexural strength (83.1%), while the specimen after 30 thermal cycles failed catastrophically without fiber pullout due to the severe oxidation damage of C/C substrate especially the brittleness of the reinforcement fibers.