Effects of TiO2 starting materials on the synthesis of Li2ZnTi3O8 for lithium ion battery anode
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Effects of TiO2 starting materials on the synthesis of Li2ZnTi3O8 for lithium ion battery anode Effects of TiO2 starting materials on the synthesis of Li2ZnTi3O8 for lithium ion battery anode](/preview/png/5438741.png)
چکیده انگلیسی
Lithium zinc titanate (Li2ZnTi3O8) anode materials have been successfully synthesized using rutile-TiO2 with different particle sizes as titanium sources via a molten-salt method. Various physical and electrochemical methods are applied to characterize the effects of TiO2 particle sizes on the structures and physicochemical properties of the Li2ZnTi3O8 materials. When the particle size of TiO2 is too small (10 nm), it is difficult to homogeneously mix TiO2 with the other raw materials. Thus, the final product Li2ZnTi3O8 has poor crystallinity, large particle size, small specific surface area, pore volume and average pore diameter, which are disadvantageous to its electrochemical performance. Using TiO2 with the proper particle size of 100 nm as the titanium source, the Li2ZnTi3O8 (R-100-LZTO) with excellent electrochemical performance can be obtained. At 1 A gâ1, 175.8 and 163.6 mA h gâ1 are delivered at the 1st and the 200th cycles, respectively. The largest capacities of 163, 133.3 and 122.5 mA h gâ1 are delivered at 2.5, 5 and 6 A gâ1, respectively. The good high-rate performance of the R-100-LZTO originates from the good crystallinity, small particle size, large specific surface area and average pore diameter, low charge-transfer resistance and high Li+ diffusion coefficient.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 42, Issue 15, 15 November 2016, Pages 16872-16881
Journal: Ceramics International - Volume 42, Issue 15, 15 November 2016, Pages 16872-16881
نویسندگان
Lijuan Wang, Zhaohui Meng, Hongwei Wang, Xinxi Li, Guoqing Zhang,