عنوان انگلیسی مقاله ISI
Synergy of corrosion-induced micro-cracking and hydrogen embrittlement on the structural integrity of aluminium alloy (Al-Cu-Mg) 2024
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Synergy of corrosion-induced micro-cracking and hydrogen embrittlement on the structural integrity of aluminium alloy (Al-Cu-Mg) 2024 Synergy of corrosion-induced micro-cracking and hydrogen embrittlement on the structural integrity of aluminium alloy (Al-Cu-Mg) 2024](/preview/png/5439902.png)
چکیده انگلیسی
Synergy of corrosion-induced micro-cracking and hydrogen embrittlement on the structural integrity of ultra-thin 2024-T3 aluminium sheets is investigated. Depth of attack of corrosion-induced cracks was experimentally measured and crack density was calculated. Stress intensity factor probability density follows the normal and lognormal distribution for the low and high exposure times, respectively. Transverse (T) rolling direction is more susceptible to corrosion attack and fracture, as 26% fracture probability was calculated after only 2Â h corrosion exposure when compared to only 11% for the Longitudinal (L) rolling direction. The synergetic mechanisms of (a) micro-cracks and (b) hydrogen embrittlement were experimentally derived from the plots of tensile ductility over depth of attack values. It was found that in the L rolling direction, 27% of the ductility decrease is attributed to the hydrogen embrittlement while the rest 73% to the micro-crack formation. For the case of T rolling direction, the respective contributions are 49% and 51% that proves its high susceptibility to corrosion attack and especially to hydrogen embrittlement.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Corrosion Science - Volume 121, June 2017, Pages 32-42
Journal: Corrosion Science - Volume 121, June 2017, Pages 32-42
نویسندگان
Nikolaos D. Alexopoulos, Christina Charalampidou, Panagiotis Skarvelis, Stavros K. Kourkoulis,