Effect of carbo-nitride-rich and oxide-rich inclusions on the pitting susceptibility of depleted uranium

The effects of carbo-nitride-rich and oxide-rich inclusions on the pitting susceptibility of depleted uranium were investigated by electrochemical corrosion measurements, optical microscopy, scanning Kelvin probe force microscopy (SKPFM), and SEM. The results of the potentiodynamic polarization tests suggest that oxide-rich inclusions are more likely to induce pitting corrosion than carbo-nitride-rich inclusions. This enhanced corrosion may be explained by the strong local galvanic coupling between the oxide-rich inclusion and the surrounding matrix, which, from the sight of SKPFM analysis, exhibits a 115 V higher Volta potential than the coupling between the carbo-nitride-rich inclusions and the matrix, respectively.