- The nonflammable Mg85Al10Ca5 alloy exhibits a high ignition temperature of 1436Â K.
- The oxide film formed on the molten alloy was found to be a three-layered structure.
- The outer layer of the three-layered structure consists of fine CaO grains.
- The incombustibility may be due to the formation of the fine CaO outer layer.
A nonflammable Mg-10Al-5Ca (at.%) alloy that can be melted in air without a cover gas or flux is developed. The alloy immediately forms a protective oxide film consisting of three layers, a fine CaO outer layer, a fine MgO intermediate layer, and a coarse MgO innermost layer. The anionic volume ratio of the CaO/MgO interface is 1.48. This interface ratio is sufficiently large to suggest the generation of a strong compressive force in the CaO layer. The dense, uniform fine CaO layer may act as a protective layer preventing the diffusion of oxygen.
334
Journal: Corrosion Science - Volume 122, 1 July 2017, Pages 118-122