Cyclic testing of thin Ni films on a pre-tensile compliant substrate

A novel experimental approach to study the cyclic plastic deformation of thin metallic films is presented. 300 nm thick Ni films are deposited on both sides of a pre-tensile soft substrate which allows to deform the films alternately in tension and compression (approximately from +2.7 GPa down to −2 GPa) relative to the as-deposited residual stress state. Nanocrystalline thin films' intrinsic elastic strains (or stresses) and true strains have been measured step by step during two loading/unloading cycles thanks to the X-ray diffraction (XRD) and digital image correlation (DIC) techniques respectively. From the first cyclic deformation, a significant Bauschinger effect is evidenced in the films, however, little or no cyclic hardening is observed during the two cyclic tests.