Deformation behavior of additively manufactured GP1 stainless steel
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
In-situ neutron diffraction measurements were performed during heat-treating and uniaxial loading of additively manufactured (AM) GP1 material. Although the measured chemical composition of the GP1 powder falls within the composition specifications of 17-4 PH steel, a fully martensitic alloy in the wrought condition, the crystal structure of the as-built GP1 material is fully austenitic. Chemical analysis of the as-built material shows high oxygen and nitrogen content, which then significantly decreased after heat-treating in a vacuum furnace at 650 °C for one hour. Significant austenite-to-martensite phase transformation is observed during compressive and tensile loading of the as-built and heat-treated material with accompanied strengthening as martensite volume fraction increases. During loading, the initial average phase stress state in the martensite is hydrostatic compression independent of the loading direction. Preferred orientation transformation in austenite and applied load accommodation by variant selection in martensite are observed via measurements of the texture development.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 696, 1 June 2017, Pages 331-340
Journal: Materials Science and Engineering: A - Volume 696, 1 June 2017, Pages 331-340
نویسندگان
B. Clausen, D.W. Brown, J.S. Carpenter, K.D. Clarke, A.J. Clarke, S.C. Vogel, J.D. Bernardin, D. Spernjak, J.M. Thompson,