Effect of crystallographic orientation on nanomechanical modelling of an iron single crystal cracked cantilever beam

Preliminary examinations in TEM of cantilever beams from machining with FIB has indicated the formation of a local brittle fracture as observed for the brittle (100)[01¯1] crack orientation in the modelling.