عنوان انگلیسی مقاله ISI
Effects of sintering additives on mechanical properties and microstructure of Si3N4 ceramics by microwave sintering
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Effects of sintering additives on mechanical properties and microstructure of Si3N4 ceramics by microwave sintering Effects of sintering additives on mechanical properties and microstructure of Si3N4 ceramics by microwave sintering](/preview/png/5456297.png)
چکیده انگلیسی
Si3N4 ceramics with excellent mechanical properties and microstructure were fabricated by microwave sintering. The effects of sintering additives on the densification, phase transformation and grain growth of Si3N4 ceramics were investigated. The results showed that Y2O3 can promote the phase transformation, MgO can decrease the sintering temperature, Al2O3 can increase the Vickers hardness of the samples and the combination of Y2O3 and MgO was more effective in enhancing the densification and phase transformation in the microwave sintering. The samples with 5 wt%Y2O3, 5 wt%MgO and 2 wt%Al2O3 sintering additives had the optimum mechanical properties when sintered at 1700 â for 10 min. Its relative density, fracture toughness and Vickers hardness were 98.52±0.13%, 6.44±0.02 MPa m1/2 and 14.92±0.20 GPa, respectively. Compared to other microwave sintered Si3N4, the hardness and fracture toughness were enhanced by 6.6-24.3% and 5.6-11%, respectively, while the sintering holding time was reduced by 33.3-83.3%.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 684, 27 January 2017, Pages 127-134
Journal: Materials Science and Engineering: A - Volume 684, 27 January 2017, Pages 127-134
نویسندگان
Weiwei Xu, Zengbin Yin, Juntang Yuan, Zhenhua Wang, Yihang Fang,