Superplasticity of Inconel 718 after processing by high-pressure sliding (HPS)
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
This study reports a production of a superplastic Ni-based superalloy (Inconel 718) using a process of severe plastic deformation through high-pressure sliding (HPS). The grain size of the alloy was reduced to ~120Â nm by operating the HPS process under 4Â GPa at room temperature with a recently upscaled facility. The ultrafined-grained structure was well retained even after annealing at 1173Â K for 1Â h. Tensile tests were conducted in air at a testing temperature in the range of 973-1173Â K with an initial strain rate of 5.0Ã10â4-2.0Ã10â2Â sâ1. Superplastic elongation more than 400% were attained at all testing conditions except at 973Â K. High-strain rate superplasticity (defined with strain rates higher than 1Ã10â2Â sâ1) was achieved at temperatures higher than 1073Â K. Electron back scatter diffraction analyses revealed that a preferential orientation of the grains was developed by the HPS processing but it was randomized with tensile deformation. Evaluation of the strain rate sensitivity and the activation energy for the superplastic deformation confirmed that the superplasticity of Inconel 718 was controlled by grain boundary sliding through lattice diffusion.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 682, 13 January 2017, Pages 603-612
Journal: Materials Science and Engineering: A - Volume 682, 13 January 2017, Pages 603-612
نویسندگان
Yoichi Takizawa, Takahiro Kajita, Petr Kral, Takahiro Masuda, Kyohei Watanabe, Manabu Yumoto, Yoshiharu Otagiri, Vaclav Sklenicka, Zenji Horita,