Studying on tempering transformation and internal friction for low carbon bainitic steel
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
Studying on tempering transformation and internal friction for low carbon bainitic steel
چکیده انگلیسی
The changes of microstructure during the process of tempering transformation were analyzed by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction and internal friction (IF) for low carbon bainite steel. The yield strength of the steel was tested after tempering transformation. The results showed that the microstructures of the experimental steel in rolled state were composed of lath bainite and granular bainite with a little Mo2C and NbC precipitates. The lath width of bainite increased continuously with the tempering time. More cell structures with different orientations were formed in bainite laths. Furthermore, poly-gonization gradually began in some laths. The microstructure of granular bainite increased and was coarsened when it devoured the lath bainite continuously. The dislocation density of the bainitic ferrite decreased continuously as Mo2C and NbC precipitations were further increasing. The peak value of Snoek decreased continuously in internal friction-temperature spectrum. The peak value of SKK at the surface decreased at first and then increased. The peak value of SKK at the center decreased firstly and then had little change. Besides, the yield strength of the steel increased firstly and then decreased.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 679, 2 January 2017, Pages 410-416