Core-rim structure formation in TiC-Ni based cermets fabricated by a combined thermal explosion/hot-pressing process
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Core-rim structure formation in TiC-Ni based cermets fabricated by a combined thermal explosion/hot-pressing process Core-rim structure formation in TiC-Ni based cermets fabricated by a combined thermal explosion/hot-pressing process](/preview/png/5457870.png)
چکیده انگلیسی
TiC-Ni-based cermets were obtained by thermal explosion from different elemental mixtures (Ti, C, Ni and X, where XÂ =Â Cr, Mo or W) and subsequently densified by hot-pressing under a cyclic load. The whole process was performed in a single stage in the same experimental device according to the following thermal and pressure procedure: a heating rate ramp up to 1573Â K without applying any load followed by an isothermal dwelling under a compressive cyclic load of 32Â MPa. The thermal explosion synthesis occurred during the heating ramp at a temperature close to 1273Â K that was practically independent of the starting nominal composition. The influence of different refractory elements on the chemical composition and microstructure of cermets was studied. SEM characterization showed that only with Mo and W, the cermets developed the characteristic core-rim structure. A high densification was achieved, but decreased when the refractory elements were added. Nevertheless, in these cases higher hardness values were obtained.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: International Journal of Refractory Metals and Hard Materials - Volume 70, January 2018, Pages 84-92
Journal: International Journal of Refractory Metals and Hard Materials - Volume 70, January 2018, Pages 84-92
نویسندگان
S. Lemboub, S. Boudebane, F.J. Gotor, S. Haouli, S. Mezrag, S. Bouhedja, G. Hesser, H. Chadli, T. Chouchane,