Ultrasonic spot welding of Al sheets by enhancing the temperature of weld interface

Ultrasonic spot welded Al/Al joints with Al2219 particle interlayer for enhancing the temperature of the weld interface were successfully conducted. The results indicate that Al2219 particle interlayer is beneficial to the increase of temperature at the weld interface, and the increased temperature further facilitates the weldability of Al/Al joints. Meanwhile, no unbonded regions are discovered, and the combination of Al/interlayer interface is high close. The peak tensile shear load of ∼5.47 kN is achieved for the joint with Al2219 particle interlayer, which is 35.7% higher than that (∼4.03 kN) for the joint without Al2219 particle interlayer.