Influence of Si content on mechanical and tribological properties of TiAlSiN PVD coatings at elevated temperatures

In this study, TiAlSiN coatings with different Si contents (0-10.9 at%) were produced by means of magnetron sputtering. In order to test the possibility to sputter pure, low conductive silicon targets, different sputter and bias modes were tested. The ratios of the other coating elements were kept constant while varying the silicon content inside the PVD coatings. Nitrided steel samples (AISI H11) were used as substrate materials. The influence of the Si content on the tribomechanical properties of TiAlSiN were analyzed. The analyses focused on the coatings with a silicon content of 5-10 at% due to the change of the coating morphology within this range. The coating morphology and different chemical compositions of the silicon-doped coatings were investigated by means of scanning electron microscopy and EDX analyses. Phase analyses were conducted and residual stresses were measured by means of X-ray diffraction. The hardness and Young's modulus of the PVD coatings were investigated using nanoindentation. Furthermore, scratch tests were performed in order to characterize the adhesion between the substrate and the coating. Finally, high temperature tribometer tests were executed to determine the wear resistance of the TiAlSiN coatings at room temperature as well as at elevated temperatures (500 °C, 800 °C).