Heterogeneous photocatalysis is a very effective method for the decomposition of a whole range of water pollutants. In this work, the influence of synthesis conditions on the physical properties and photocatalytic activity of lanthanide-doped titanium dioxide photocatalysts was evaluated. Titanium dioxide was prepared via sol-gel synthesis followed by a solid state reaction under different conditions, including different temperatures (450, 550, and 650 °C) and reaction times (4, 8, and 12 h). The crystalline phase of the products was determined to be solely anatase using X-ray diffraction, and this result was confirmed by Raman spectroscopy. The structure, as well as particle size, of the samples was examined using scanning electron microscopy, and their specific surface area was calculated using Brunauer-Emmett-Teller analysis. The band gap energy of the samples was examined using ultraviolet-visible spectroscopy from diffuse reflectance measurements. Doping with lanthanide species, dysprosium and praseodymium, caused the absorption edge to shift towards higher wavelengths and enhanced photocatalytic activity in comparison with pure titania. The photocatalytic activity of the samples was studied in terms of the degradation of the commonly used herbicide metazachlor. The decomposition was carried under UV light and the decrease in metazachlor concentration was measured using high performance liquid chromatography. The best performance was obtained for samples treated at 550 °C for 8 h during the solid state reaction step.
Graphical AbstractPraseodymium-doped titania shows higher photocatalytic activity than P25. The synthesis conditions significantly affected the physical properties of the photocatalysts and consequently their activity, which was mainly dependent on specific surface area.Figure optionsDownload as PowerPoint slide
Journal: Chinese Journal of Catalysis - Volume 36, Issue 10, October 2015, Pages 1679–1684