Multi-pass scratch test behavior of modified layer formed during plasma nitriding

316L stainless steel and Ti6Al4V alloy were plasma nitrided at different treatment parameters, and the wear behaviors of the modified layers formed on the surface during nitriding were investigated by multi-pass scratch test. Phase structure and cross-sections of modified layers were also examined with XRD and SEM. While a single modified layer formed on surface of the 316L stainless steel, both modified and diffusion layers were observed on the surface of the Ti6Al4V alloy after nitriding. As a result, it was observed that phase structure and thickness for modified layers of 316L stainless steel and Ti6Al4V alloy, respectively, were the significant parameters for friction coefficient and wear rate. In addition, diffusion layer formed during the nitriding process caused on increase of wear resistance of Ti6Al4V alloy by supporting the modified layer on the surface.