Hydrogen permeability of SrCe0.7Zr0.25Ln0.05O3−δ membranes (Ln=Tm and Yb)

• Zr stabilized acceptor doped SrCeO3membrane materials were characterized.
• Hydrogen flux was measured under open and short circuit conditions.
• De-mixing of the materials was observed after hydrogen flux measurements.

Zr substituted acceptor doped SrCeO3 materials were synthesized by citric acid route and characterized by XRD and SEM. The hydrogen flux of the materials was measured as a function of temperature and hydrogen partial pressure on the feed side. The hydrogen permeability for SrCe0.7Zr0.25Tm0.05O3−δ and SrCe0.7Zr0.25Yb0.05O3−δ is similar under our measurement window and shows the same hydrogen partial pressure dependency. Under short circuit condition, the hydrogen permeability increased significantly by more than one order of magnitude indicating that the hydrogen transport is limited by electronic conduction under open circuit conditions. The observed data were discussed by applying defect chemistry and the conventional ambipolar transport theory. After the hydrogen permeation measurements, the indication of kinetic cation de-mixing was found by XRD analysis.