• The modified bilayer membrane showed high H2 selectivity over CO, CO2 and H2O.
• The modified bilayer membrane showed excellent long-term hydrothermal stability for WGS reaction.
• The modified bilayer membrane demonstrated unprecedented chemical stability in the presence of 400 ppm H2S.
Stable inorganic membranes perm-selective to hydrogen will find applications in a number of important industrial processes including water gas shift reaction for hydrogen production. This paper reports a highly stable bilayer MFI zeolite membrane with good hydrogen separation characteristics. The membrane consists of a thin (2 μm) ZSM-5 layer on a thick (8 μm) silicalite base layer supported on macroporous α-alumina with a yttria stabilized zirconia intermediate barrier layer. The zeolitic pores of the thin ZSM-5 layer were narrowed by catalytic cracking deposition (CCD). At 500 °C, the bilayer zeolite membrane exhibits H2 permeance of about 1.2×10−7 mol m−2 s−1 Pa−1, with H2 to CO2, CO and H2O vapor selectivity respectively of about 23, 28 and 180. The membrane shows slightly improved separation properties (H2 permeance, H2/CO and H2/CO2 selectivity) as the feed side pressure increases during the test of separation of industrial relevant simulated gas mixture (25% H2: 25% CO: 25% H2O: 25% CO2, with 400 ppm H2S) at 500 °C for 24 days. Membrane reactor made of the bilayer zeolite membrane shows stable performance under water gas shift reaction conditions (500 °C, H2O/CO=3, GHSV=60,000 h−1, with a ceria doped iron oxide catalyst) in terms of CO conversion, H2 recovery, and H2 permeance and selectivity of the zeolite membrane. The unprecedented thermal and chemical stability and good separation properties of the bilayer zeolite membrane are related to its unique bilayer structure and synthesis methods.
Figure optionsDownload high-quality image (458 K)Download as PowerPoint slide
Journal: Journal of Membrane Science - Volume 450, 15 January 2014, Pages 425–432