عنوان انگلیسی مقاله ISI
Performance of zinc-doped perovskite-type membranes at intermediate temperatures for long-term oxygen permeation and under a carbon dioxide atmosphere
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی شیمی
تصفیه و جداسازی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Performance of zinc-doped perovskite-type membranes at intermediate temperatures for long-term oxygen permeation and under a carbon dioxide atmosphere Performance of zinc-doped perovskite-type membranes at intermediate temperatures for long-term oxygen permeation and under a carbon dioxide atmosphere](/preview/png/636726.png)
چکیده انگلیسی
Zinc-doped (BaSr)FeO3âδ perovskite-type membranes were found to exhibit excellent long-term stability at high and intermediate temperatures under an oxygen partial pressure difference of p1/p2 = 21/2.1 Ã 103 Pa at 950 °C and p1/p2 = 21/0.8 Ã 103 Pa at 750 °C. After the change to carbon dioxide as the sweep gas, the oxygen permeation diminishes almost completely. By XRD, a phase mixture of hexagonal, tetragonal and cubic perovskite with a (Ba0.4±0.1Sr0.6±0.1)CO3 layer and some zinc oxide was found. TEM showed that the dense perovskite membrane is decomposed into phases with different morphologies accompanied by pore and crack formation in a surface layer with a depth of approximately 5 μm. After switching to helium as the sweep gas, the carbonate layer is decomposed, but a hexagonal and tetragonal perovskite phase in addition to the cubic phase are still present. A short heating to 950 °C regenerates the oxygen permeation flux due to the abatement of hexagonal perovskite for the benefit of the cubic and tetragonal perovskite phase. The appearance of the carbonate structure, even to a small amount of 8%, leads to a breakdown of the oxygen permeation ability, but also the hexagonal perovskite is disadvantageous. In contrast, the cubic and tetragonal perovskite modifications exhibit good oxygen permeation abilities. The effect of the carbon dioxide is totally reversible after a short high temperature treatment.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Membrane Science - Volume 344, Issues 1â2, 15 November 2009, Pages 62-70
Journal: Journal of Membrane Science - Volume 344, Issues 1â2, 15 November 2009, Pages 62-70
نویسندگان
Julia Martynczuk, Konstantin Efimov, Lars Robben, Armin Feldhoff,