A thin and compact mesoporous MCM-48 membrane had been successfully synthesized on vacuum-coated α-Al2O3 support with pore size of 1 μm. The pretreated supports and the membranes were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and single gas permeation test. The pretreated supports were gas permeable for N2 and the as-synthesis membrane was gas tight, indicating that the defects left in the vacuum step disappeared in the multi-hydrothermal synthesis process. The XRD pattern of the membrane was represented to the typical cubic Ia3¯d space group. And the SEM images showed that the membrane was continuous and 4-μm thick. Additionally, the separation factor of the calcined membrane for H2/N2 was up to 3.33 and the Knudsen contribution to the total flux for N2 permeation was 97.8%. All the results indicated that the good surface conditions of the large-pore supports improved by the vacuum coating method were favorable for the formation of a compact MCM-48 membrane on it.
Journal: Journal of Membrane Science - Volume 319, Issues 1–2, 1 July 2008, Pages 231–237