![عکس صفحه اول مقاله: Research PaperHydrogenation of levulinic acid to γ-valerolactone over anatase-supported Ru catalysts: Effect of catalyst synthesis protocols on activity Research PaperHydrogenation of levulinic acid to γ-valerolactone over anatase-supported Ru catalysts: Effect of catalyst synthesis protocols on activity](/preview/png/6453216.png)
- Catalyst preparation protocols strongly affect catalyst performance of Ru on titania (anatase) for the hydrogenation of levulinic acid.
- Highest activity was obtained for a RuNO(NO3)3 precursor without an intermediate calcination step and 10% hydrogen in the reduction gas.
- The information can be used to prepare improved Ru based catalysts for the catalytic hydrogenation of levulinic acid .
γ-Valerolactone (GVL) is a value-added renewable chemical with great potential and can be obtained from biomass by the hydrogenation of levulinic acid (LA) using metal-based catalysts, such as Ru/TiO2. We here report an in depth study of the effect of catalyst synthesis parameters on the performance of Ru/TiO2 (anatase), varying the nature of the Ru-precursor and the conditions of the calcination and/or reduction step. Catalyst performance was evaluated under batch conditions at a hydrogen pressure of 45 bar and using either water (90 °C) or dioxane (150 °C) as solvent. The experiments showed that catalyst activity depends greatly on the Ru precursor used (RuCl3, RuNO(NO3)3, Ru(NH3)6Cl3). Best results when considering the turn-over frequencies (TOF) of the catalysts were obtained using the RuNO(NO3)3 precursor, whereas RuCl3 performed better when considering the initial rate based on Ru intake. An intermediate calcination step and the use of a hydrogen-rich sweep gas during the final reduction step were shown to have a negative impact on catalyst activity. Characterization of the fresh catalysts by BET and TEM provided valuable insight in the relation between the catalyst structure and its activity.