کد مقاله | کد نشریه | سال انتشار | مقاله انگلیسی | نسخه تمام متن |
---|---|---|---|---|
6716220 | 1428743 | 2018 | 9 صفحه PDF | دانلود رایگان |
عنوان انگلیسی مقاله ISI
Effect of temperature on bond characteristics of geopolymer concrete
ترجمه فارسی عنوان
اثر دما بر روی ویژگی های پیوند بتن ژئوپلیمر
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
ویژگی های باند، بتن ژئوپلیمر، آربار، درجه حرارت بالا، تست کشش،
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی عمران و سازه
چکیده انگلیسی
This paper presents experimental results on the bond behavior between geopolymer concrete and rebar. Pull-out tests on geopolymer concrete specimens embedded with plain and ribbed rebars were carried out at ambient temperature and after exposure to 100, 300, 500 and 700â¯Â°C. Two batches of geopolymer concrete with compressive strength of 48 and 64â¯MPa respectively, and five rebar diameters (of 10, 12, 14, 18 and 25â¯mm) were used for preparing the test specimens. Comparative benchmark tests were also conducted on ordinary Portland cement (OPC) concrete specimens. Results from these tests show that geopolymer concrete exhibits insignificant reduction in bond strength till exposure to 300â¯Â°C, but undergoes significant degradation beyond 300â¯Â°C. Data from the tests indicate that rate of bond strength degradation in geopolymer concrete is close to that of splitting tensile strength, but higher than that of compressive strength. Also, results infer that geopolymer concrete exhibits similar or better bond properties than OPC concrete, both at ambient temperature and after exposure to elevated temperatures. Thus geopolymer concrete can be a practical alternative to OPC concrete in reinforced concrete structures when fire resistance is one of the main design considerations.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Construction and Building Materials - Volume 163, 28 February 2018, Pages 277-285
Journal: Construction and Building Materials - Volume 163, 28 February 2018, Pages 277-285
نویسندگان
Hai Yan Zhang, Venkatesh Kodur, Bo Wu, Jia Yan, Zhen Sheng Yuan,