A new method to synthesize high solid content waterborne polyurethanes by strict control of bimodal particle size distribution

• A novel method was developed to synthesize WPUs with bimodal PSD.
• The bimodal PSD of WPUs can be strictly controlled including the diameter ratio and volume ratio.
• WPUs with bimodal PSD will effectively increase the packing efficiency of particles.
• High solid content (55%) and low viscosity (489.1 mPa s−1) WPU was finally obtained.

A new method named two-step emulsification process was developed to synthesize high solid content waterborne polyurethanes by strict control of the bimodal particle size distribution. In the first step, a series of 40% solid content polyester-based (WPU-1) with low content of hydrophilic group and large particle size were firstly synthesized. In the second step, polyether-based prepolymers (WPU-2 prepolymers) with high content of hydrophilic group were firstly prepared and WPU-1 emulsions were used to emulsify WPU-2 prepolymers to obtain the final emulsions with high solid content (WPU-3). The particle size of WPU-3 present bimodal distribution and the diameter ratio and volume percentage of large particles to small particles in WPU-3 were able to be strictly controlled by this method. The viscosity of WPU-3 with 55% solid content was only 489.1 mPa s−1 when the diameter ratio of large particles to small particles was 9.2 and the volume percentage of large particles was 74%.

Figure optionsDownload as PowerPoint slide