Isocyanurate based fluorinated polyurethane dispersion for anti-graffiti coatings

Fluorinated polyurethane dispersions (FPUDs) were synthesized using HDI isocyanurate, polyester polyol and DMPA with varying concentrations of trifluoro ethanol (TFE) in the range of 0–9 wt%. Further FPUDs were characterized by FT-IR and 1H NMR for structural elucidation. Effects of trifluoro ethanol on the dispersion were evaluated by particle size analyzer. It was observed that with increase in TFE, particle size increases. Topography and contact angle were studied by atomic force microscopy (AFM) and goniometer, respectively. To gain more insight into the formation of roughness, power spectral density (PSD) analysis was carried out. It was found that with increase in TFE content, surface roughness increases due to migration of fluorinating agent on the coating substrate and consequently water repellency increases. Nano indentation of coating revealed that fluorinated coating possesses less stiffness and elastic modulus, due to the presence of fluorine on the coating. Further, coatings were analyzed for thermal properties by thermogravimetry analysis (TGA) and differential scanning calorimetry (DSC) which shows the enhancement in thermal stability and glass transition temperature with increase in TFE content. Anti-graffiti test was carried out which showed improved resistance with increasing fluorine content.

Figure optionsDownload as PowerPoint slideHighlights
► 1K fluorinated polyurethane dispersion synthesized from HDI isocyanurate.
► Presence of fluorine offers anti-graffiti properties to the coating and isocyanurate imparts good mechanical properties due to crosslinking.
► Topographic study is carried with AFM and power spectral density.