Two types of phosphate fillers (nanosized aluminum phosphate and microsized aluminum–zinc phosphate) were tested as anticorrosive fillers in 2 K solvent-borne polyurethane paints based on commercial acrylic resin with OH groups and an isophorone diisocyanate-type hardener. Three coating compositions containing commercial fillers (mica/quartz, TiO2, wollastonite, talc) and also mentioned nanosized aluminum phosphate or microsized aluminum–zinc phosphate were prepared using a pearl-mill as well as a laboratory dissolver, applied onto a steel substrate and cured at room temperature for 14 days. An influence of the type and content of a phosphate filler on properties of polyurethane paints and coatings has been investigated. Incorporation of nanosized aluminum phosphate into coating compositions increases their viscosity while cured paints exhibit reduced adhesion to steel substrates. The results of corrosion tests in a salts spray chamber as well as immersion in an aqueous NaCl solution indicated that the paint system with 9.8 wt.% of applied nanofiller had similar protective properties to a polyurethane coat containing a higher dose (i.e. 15.6 wt.%) of commercial microsized aluminum–zinc phosphate.
► Nanosized Al phosphate and microsized Al–Zn phosphate as anticorrosive fillers in paints.
► Nanosized Al phosphate improves hardness and reduces adhesion of coats to steel substrates.
► Nanosized Al phosphate has better protective properties than microsized Al–Zn phosphate.
Journal: Progress in Organic Coatings - Volume 74, Issue 1, May 2012, Pages 151–157