Nanocrystalline diamond (NCD) films were deposited on Si substrates by microwave plasma-enhanced chemical vapor deposition (MPECVD) using methane/hydrogen/oxygen (30/169/0.2 sccm) as process gases. Subsequently a thin (0.33 μm) and a thick (1.01 μm) NCD films were irradiated with XeF excimer laser (λ = 351 nm) with 300 and 600 mJ cm− 2 of energy densities in air. The NCD films became rougher after laser irradiations. Fraction of graphitic clusters decreased but oxygen content increased in the thin NCD film after laser irradiation. Opposite phenomena were observed for the thick NCD films. Effect of laser irradiation to oxygenation and graphitization of NCD films was correlated with structural properties of free surface and grain boundaries of the thin and thick NCD films.
Journal: Diamond and Related Materials - Volume 19, Issues 5–6, May–June 2010, Pages 445–448