In this report, the FE characteristics of carbon nanotubes (CNTs) treated using both thermal annealing and mechanical coatings on the as-grown CNTs systematically studied. It was found that in the high temperature annealed samples, CNTs were attacked at its root during annealing due to a small amount of oxygen, and were pulled out of the substrate in places after FE measurements because of the contact resistance. However, for the mechanically coated samples both with spin on glass (SOG) and polymethyl methacrylate (PMMA), CNTs were found to be nearly intact after FE measurements and showed reliable FE characteristics over repeatable voltage scan. The reliability of CNTs during FE could be owing to the strong adhesion of CNTs to the substrate both by SOG and PMMA coatings.
Journal: Diamond and Related Materials - Volume 14, Issues 11–12, November–December 2005, Pages 1891–1896