Radiation tolerance of type IIa synthetic diamond detector for 14 MeV neutrons

Radiation tolerance of a type IIa synthetic diamond detector was examined from irradiation of mono-energetic 14 MeV neutrons. Measurements of I–V (current–voltage) characteristics and energy spectrum for 5.486 MeV alpha particles were performed after neutron irradiation. In the I–V characteristics measurement, enhancement of rectification was observed after neutron irradiation of up to 2.0 × 1012 n/cm2. Concurrently with the enhancement of rectification, significant decrease in signal amplitude was observed in energy spectrum measurement for alpha particles. It is considered that these changes were due to increase in the concentration of defects acting as shallow energy levels in the forbidden band. For neutron irradiation of higher than 1.6 × 1013 n/cm2, weakening of the rectification characteristics and recovery of the signal amplitude were observed. These changes imply that deep energy levels, which were also considered to be introduced by defects, were dominant and weakened the effects of the shallow energy levels. Increase in the concentration of the deep trapping levels resulted in gradual decrease of the signal amplitude and degradation in the energy resolution. The peak for the alpha particles was obtained up to 5.5 × 1013 n/cm2.