The hydrogenated amorphous carbon films doped with Ti and Si ((Ti,Si)–C:H) were deposited on silicon substrates using reactive magnetron sputtering Ti80Si20 composite target in an argon and methane gas mixture. The structures of the films were analyzed by X-ray photoelectron spectroscopy and Visible Raman spectroscopy. The morphologies were observed by atomic force microscope. The friction coefficients of the films were tested on the ball-on-disc tribometer. The results indicate that the sp3/sp2 ratios in the films can be varied from 0.18 to 0.63 by changing Ti and Si contents at various CH4 flow rates. The surface of the films becomes smoother and more compact as the CH4 flow rate increases. The lowest friction coefficient is as low as 0.0139 for the film with Ti of 4.5 at.% and Si of 1.0 at.%. Especially, the film exhibits a superlow value (μ < 0.01) under ambient air with 40% relative humidity in friction process. The superlow friction coefficient in ambient air may be, attributable to synergistic effects of a combination of Ti and Si in the film.
Journal: Diamond and Related Materials - Volume 19, Issue 10, October 2010, Pages 1172–1177