Fatigue crack initiation and growth in 43Fe-25Ni-22.5Cr austenitic steel at a temperature of 700â¯Â°C
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی مکانیک
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Fatigue crack initiation and growth in 43Fe-25Ni-22.5Cr austenitic steel at a temperature of 700â¯Â°C Fatigue crack initiation and growth in 43Fe-25Ni-22.5Cr austenitic steel at a temperature of 700â¯Â°C](/preview/png/7171373.png)
چکیده انگلیسی
Crack initiation and short crack growth in highly-alloyed austenitic steel Sanicro 25 cyclically strained at a temperature of 700â¯Â°C has been studied. Specimens cycled to 10% of the fatigue life and to the fracture were inspected using scanning electron microscopy and electron backscatter diffraction. On the surface, thin lamellae were extracted site-specifically by focused ion beam and then they were further characterized by high spatial resolution scanning transmission electron microscopy and energy dispersive X-ray spectroscopy. The preferential oxidation of grain boundaries was found to play a principal role in the initiation of multiple cracks. The oxide scale was analysed to show the distribution of individual elements during crack initiation and growth. Two types of crack paths were observed: intergranular due to the oxidation and transgranular accompanied by a cyclic plastic zone. Cracks preferentially initiated at the grain boundaries perpendicular to the stress axis and propagated in the bulk of the material. The role of the oxidation in high temperature fatigue crack initiation is discussed as well as the mechanisms of the crack initiation and growth.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: International Journal of Fatigue - Volume 114, September 2018, Pages 11-21
Journal: International Journal of Fatigue - Volume 114, September 2018, Pages 11-21
نویسندگان
V. Mazánová, M. Heczko, J. Polák,