Fatigue behaviour at elevated temperature of friction stir channelling solid plates of AA5083-H111 aluminium alloy

Based on the fracture surfaces observations, the developing fatigue-crack always initiated at the advancing side, namely on the boundary between the nugget and the thermo-mechanically affected zone into the interior of the specimen.