Selective catalytic methanation of CO in hydrogen-rich gases over Ni/ZrO2 catalyst

Ni/ZrO2 catalysts were prepared by the incipient-wetness impregnation method and were investigated in activity and selectivity for the selective catalytic methanation of CO in hydrogen-rich gases with more than 20 vol% CO2. The result showed that Ni loadings significantly influenced the performance of Ni/ZrO2 catalyst. The 1.6 wt% Ni loading catalyst exhibited the highest catalytic activity among all the catalysts in the selective methanation of CO in hydrogen-rich gas. The outlet concentration of CO was less than 20 ppm with the hydrogen consumption below 7%, at a gas-hourly-space velocity as high as 10000 h−1 and a temperature range of 260 °C to 280 °C. The X-ray diffraction (XRD) and temperature programmed reduction (TPR) measurements showed that NiO was dispersed thoroughly on the surface of ZrO2 support if Ni loading was under 1.6 wt%. When Ni loading was increased to 3 wt% or above, the free bulk NiO species began to assemble, which was not favorable to increase the selectivity of the catalyst.