Modeling of combined capacity fade with thermal effects for a cycled LixC6-LiyMn2O4 cell

► Modeling of thermal and capacity fade effects for a LixC6-LiyMn2O4 cell. ► Capacity fade effects at anode and cathode were found to be significant during cycling. ► SEI formation operates under steady-state conditions during battery cycling. ► Degradation of the cell is more prominent during the dissolution of LiyMn2O4 particles.