Nitrogen-doped porous carbon from Camellia oleifera shells with enhanced electrochemical performance
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
بیومتریال
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Nitrogen-doped porous carbon from Camellia oleifera shells with enhanced electrochemical performance Nitrogen-doped porous carbon from Camellia oleifera shells with enhanced electrochemical performance](/preview/png/7868218.png)
چکیده انگلیسی
Nitrogen doped porous activated carbon was prepared by annealing treatment of Camellia oleifera shell activated carbon under NH3. We found that nitrogen content of activated carbon up to 10.43 at.% when annealed in NH3 at 800 °C. At 600 °C or above, the N-doped carbon further reacts with NH3, leads to a low surface area down to 458 m2/g and low graphitization degree. X-ray photoelectron spectroscope (XPS) analysis indicated that the nitrogen functional groups on the nitrogen-doped activated carbons (NACs) were mostly in the form of pyridinic nitrogen. We discovered that the oxygen groups and carbon atoms at the defect and edge sites of graphene play an important role in the reaction, leading to nitrogen atoms incorporated into the lattice of carbon. When temperatures were lower than 600 °C the nitrogen atoms displaced oxygen groups and formed nitrogen function groups, and when temperatures were higher than 600 °C and ~ 4 at.% carbon atoms and part of oxygen function groups reacted with NH3. When compared to pure activated carbon, the nitrogen doped activated carbon shows nearly four times the capacitance (191 vs 51 F/g).
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: C - Volume 61, 1 April 2016, Pages 449-456
Journal: Materials Science and Engineering: C - Volume 61, 1 April 2016, Pages 449-456
نویسندگان
Yunbo Zhai, Bibo Xu, Yun Zhu, Renpeng Qing, Chuan Peng, Tengfei Wang, Caiting Li, Guangming Zeng,