Effect of calcium sulfate source on the hydration of calcium sulfoaluminate eco-cement
ترجمه فارسی عنوان
تأثیر منبع سولفات کلسیم بر میزان هیدراتاسیون الکترو سیمان کلسیم سولفالومینات
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی صنعتی و تولید
چکیده انگلیسی
The availability of cements, including eco-cements, with tailored mechanical properties is very important for special applications in the building industry. Here we report a full study of the hydration of calcium sulfoaluminate eco-cements with different sulfate sources (gypsum, bassanite and anhydrite) and two water/cement ratios (0.50 and 0.65). These parameters have been chosen because they are known to strongly modify the mechanical properties of the resulting mortars and concretes. The applied multi-technique characterization includes: phase assemblage by Rietveld method, evolved heat, conductivity, rheology, compressive strength and expansion/retraction measurements. The dissolution rate of the sulfate sources is key to control the hydration reactions. Bassanite dissolves very fast and hence the initial setting time of the pastes and mortars is too short (20 min) to produce homogeneous samples. Anhydrite dissolves slowly so, at 1 hydration-day, the amount of ettringite formed (20 wt%) is lower than that in gypsum pastes (26 wt%) (w/c = 0.50), producing mortars with lower compressive strengths. After 3 hydration-days, anhydrite pastes showed slightly larger ettringite contents and hence, mortars with slightly higher compressive strengths. Ettringite content is the chief parameter to explain the strength development in these eco-cements.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Cement and Concrete Composites - Volume 55, January 2015, Pages 53-61
Journal: Cement and Concrete Composites - Volume 55, January 2015, Pages 53-61
نویسندگان
Marta GarcÃa-Maté, Angeles G. De la Torre, Laura León-Reina, Enrique R. Losilla, Miguel A.G. Aranda, Isabel Santacruz,