Synthesis of CsxWO3 nanoparticles and their NIR shielding properties
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Synthesis of CsxWO3 nanoparticles and their NIR shielding properties Synthesis of CsxWO3 nanoparticles and their NIR shielding properties](/preview/png/7886239.png)
چکیده انگلیسی
A simple two-step route is developed to fabricate hexagonal CsxWO3 nanoparticles. The core of this route is the preparation of the precursor by drying the mixture of WO3 sol and CsCl, which leads to a higher Cs/W (0.32) ratio at low temperature in a short time. During reaction, oleic acid, used as a solvent, can be adsorbed on the surface of CsxWO3 nanoparticles, which results in small particle size (20â¯nmâ¯Ãâ¯10â¯nm) and mild agglomeration. In addition, oleic acid also plays a role as a reducing agent in forming CsxWO3 nanoparticles without any further post-treatment. Furthermore, the film prepared from as-synthesized Cs0.32WO3 nanoparticles shows excellent NIR-shielding properties (approximately 99% of the near-infrared radiation is cut off over a wavelength range of 780-2600â¯nm and the visible-light transmittance at 465â¯nm is 78.9%) when covering on an ordinary sheet of glass. A model which simulates the real environment is applied to evaluate heat-shielding performance of the Cs0.32WO3 film while comparing with that of ordinary glass and commercial ITO glass (10â¯Î© â¡â1). Results revealed that the Cs0.32WO3 film showed superior performance than others.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 44, Issue 12, 15 August 2018, Pages 13469-13475
Journal: Ceramics International - Volume 44, Issue 12, 15 August 2018, Pages 13469-13475
نویسندگان
Yongji Yao, Liangmiao Zhang, Zhang Chen, Chuanxiang Cao, Yanfeng Gao, Hongjie Luo,