Modeling the cracking of cover concrete due to non-uniform corrosion of reinforcement

In situations when external chloride penetration is the cause of depassivation, the corrosion process may start from the outer region of a rebar, which might expand non-uniformly. Therefore, the main objective of the present work is to explore the effect of non-uniform corrosion on cracking behavior of cover concrete. The influences of concrete heterogeneities and the porous layer generated at the rebar/concrete interface on the failure patterns and the corrosion level of cover concrete are considered. The random aggregate structures of concrete are built, and the concrete is regarded as a composite composed of three phases, i.e. the aggregate, mortar matrix, and the interfacial transition zones (ITZs). The plasticity damaged model is employed to describe the mechanical properties of the mortar matrix and the ITZs, and it is assumed that the aggregate is elastic. Non-uniform radial displacement with a half ellipse shape is adopted to describe the expansion distribution of the corrosion products. The failure pattern and the corrosion pressure of cover concrete, and the critical corrosion level when the cover concrete cracks due to non-uniform corrosion expansion are studied based on the meso-scale numerical method. The comparison of the simulation results with the available test results on the failure pattern of cover concrete shows fairly good agreement. Moreover, the influence of meso-structural heterogeneities is explored, and the cracking behavior obtained under non-uniform and uniform expansion conditions are compared. Finally, the influences of cover thickness, rebar diameter and the location of rebar (namely side-located rebar and corner-located rebar), on the failure pattern and the corrosion level are examined.