Intergranular corrosion behavior associated with delta-ferrite transformation of Ti-modified Super304H austenitic stainless steel

A double loop electrochemical potentiokinetic reactivation (DL-EPR) test was conducted to investigate the relationship between the evolution of delta-ferrite and the intergranular corrosion (IGC) of Ti-modified Super304H, which was aged at 650 °C for 4-500 h. Scanning electron microscopy and transmission electron microscopy were adopted to analyze the evolution of delta-ferrite. The results indicated that a higher fraction of delta-ferrite with poor stability increased the IGC sensitisation of Ti-modified Super304H. Moreover, the self-healing of the sensitisation of Ti-modified Super304H occurred after 48 h due to the diffusion of chromium atoms mainly from the adjacent primary austenite rather than the delta-ferrite.