Effect of applied potential on passivation and erosion-corrosion of a Fe-based amorphous metallic coating under slurry impingement

The passive behaviour and erosion-corrosion behaviour of a HVOF sprayed Fe-based amorphous metallic coating have been investigated in 3.5 wt.% NaCl solution by using potentiostatic polarisation, X-ray photoelectron spectroscopy and Mott-Schottky analysis. The fact that passive current density increased with rising potential might result from the preferential dissolution of high-valence oxides and the existence of more chlorides at a higher potential. The critical flow velocity decreased with rising potential because of the lower resistance of passive film at a higher potential. The reason why passive current density changed under jet impingement was discussed by a simple formula.