Effects of alkali metal oxides on crystallization behavior and acid corrosion resistance of cordierite-based glass-ceramics
ترجمه فارسی عنوان
اثرات اکسید فلزات قلیایی بر رفتار بلوری و مقاومت به خوردگی اسید سرامیک بر پایه کوردیریت
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
اکسید فلزی قلیایی، بلورسازی، مقاومت اسیدی، سرامیک شیشه ای،
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
چکیده انگلیسی
MgO-Al2O3-SiO2-TiO2 glass-ceramics with 3 mol% alkali metal oxides were prepared, and the 3 mol% alkali metal oxides were induced by 3 mol% Na2O only, 1.5 mol% Na2O + 1.5 mol% Li2O, and 1.5 mol% Na2O + 1.5 mol% K2O, respectively. Effects of alkali metal oxides on the crystallization behavior and acid corrosion resistance of the MgO-Al2O3-SiO2-TiO2 glass-ceramics were investigated. The results showed that μ-cordierite precipitated in the glass matrix firstly, and it changed into α-cordierite with the crystallization temperature increasing. Using K2O substitution of Na2O hindered the precipitation of cordierite, while the addition of Li2O promoted the precipitation of μ-cordierite at low temperatures. When the main crystalline phase was μ-cordierite, the acid resistance of the glass-ceramics was significantly improved compared with the base glass. With the main crystalline phase changing from μ-cordierite to α-cordierite, the acid resistance of the glass-ceramics became worse, which was related to the honeycomb structure of α-cordierite. When 1.5 mol% Na2O was replaced by Li2O, the glass samples crystallized at 880 °C showed the optimum acid resistance with the minimum weight loss ~ 0.096%.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Non-Crystalline Solids - Volume 481, 1 February 2018, Pages 184-190
Journal: Journal of Non-Crystalline Solids - Volume 481, 1 February 2018, Pages 184-190
نویسندگان
Junfeng Kang, Jing Wang, Xinyan Zhou, Jian Yuan, Yansheng Hou, Shaoyang Qian, Sheng Li, Yunlong Yue,