Current endovascular stents have sub-optimal biocompatibility reducing their clinical efficacy. We previously demonstrated a plasma-activated coating (PAC) that covalently bound recombinant human tropoelastin (TE), a major regulator of vascular cells in vivo, to enhance endothelial cell interactions. We sought to develop this coating to enhance its mechanical properties and hemocompatibility for application onto coronary stents. The plasma vapor composition was altered by incorporating argon, nitrogen, hydrogen or oxygen to modulate coating properties. Coatings were characterized for 1) surface properties, 2) mechanical durability, 3) covalent protein binding, 4) endothelial cell interactions and 5) thrombogenicity. The N2/Ar PAC had optimal mechanical properties and did not delaminate after stent expansion. The N2/Ar PAC was mildly hydrophilic and covalently bound the highest proportion of TE, which enhanced endothelial cell proliferation. Acute thrombogenicity was assessed in a modified Chandler loop using human blood. Strikingly, the N2/Ar PAC alone reduced thrombus weight by ten-fold compared to 316L SS, a finding unaltered with immobilized TE. Serum soluble P-selectin was reduced on N2/Ar PAC and N2/Ar PAC + TE (p < 0.05), consistent with reduced platelet activation. We have demonstrated a coating for metal alloys with multifaceted biocompatibility that resists delamination and is non-thrombogenic, with implications for improving coronary stent efficacy.
Journal: Biomaterials - Volume 31, Issue 32, November 2010, Pages 8332–8340