Deformation mechanisms of Al0.1CoCrFeNi high entropy alloy at ambient and cryogenic temperatures
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Deformation mechanisms of Al0.1CoCrFeNi high entropy alloy at ambient and cryogenic temperatures Deformation mechanisms of Al0.1CoCrFeNi high entropy alloy at ambient and cryogenic temperatures](/preview/png/7971681.png)
چکیده انگلیسی
The deformation mechanisms of an Al0.1CoCrFeNi high entropy alloy (HEA) produced by the vacuum levitation melting (VLM) method were studied in the compression test at temperatures range from 298â¯K to 77â¯K. The nominal yield strength was 120, 168, 275â¯MPa for the alloy tested at 298, 200, and 77â¯K, respectively. Note that all the compression tests were done only up to the ~ 50% plastic strains. In addition, the remarkable strain-hardening ability and the serration phenomena were observed during the deformation of the alloy at 77â¯K. Transmission electron microscopy (TEM) and high-resolution TEM (HRTEM) characterizations revealed that at 298 and 200â¯K, the deformation in the alloy occurs on the normal FCC {111}<â¯110â¯>â¯slip systems by planar dislocation glide. In contrast, at 77â¯K, nano-twinning becomes an additional deformation mechanism. Overall, the significant increase in the nominal yield strength, extensive strain-hardening ability, and the serration phenomena are attributed to the capability of extensive nano-twinnings at 77â¯K.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 733, 22 August 2018, Pages 408-413
Journal: Materials Science and Engineering: A - Volume 733, 22 August 2018, Pages 408-413
نویسندگان
Songqin Xia, Yong Zhang,