Evolution of microstructure and mechanical properties of coated Co-base superalloys during heat treatment and thermal exposure

New γ′-strengthened Co-base superalloys show an interesting potential for high temperature applications. However, protective coatings are needed as for Ni-base superalloys to ensure sufficient oxidation and corrosion resistance. Therefore the properties of a commercial coating on a multinary new γ′-strengthened Co-base superalloy have been studied. Especially the influence of the coating process on the substrate also after long term annealing is discussed. It was found that the highly deformed areas at the coating-substrate interface indicated by a high local misorientation and caused by the sandblasting process led to a recrystallization of the interdiffusion zone during the age hardening heat treatment. A chemical gradient of γ and γ′ promoting elements was found in the interdiffusion zone causing a change in hardness as measured by nanoindentation. Depending on the composition two separate recrystallized regions formed in the interdiffusion zone, one with single phase γ-(Co,Ni) and the other with a cellular two phase microstructure of discontinuously grown γ and γ′.