Effects of Ag variations on the microstructures and mechanical properties of Al-Cu-Mg alloys at elevated temperatures
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Effects of Ag variations on the microstructures and mechanical properties of Al-Cu-Mg alloys at elevated temperatures Effects of Ag variations on the microstructures and mechanical properties of Al-Cu-Mg alloys at elevated temperatures](/preview/png/7980994.png)
چکیده انگلیسی
Microstructures and mechanical properties of Al-Cu-Mg alloys containing various Ag additions were investigated by a combination of the tensile testing and quantitative transmission electron microscopy (TEM) analysis. Our results indicated that an increase of Ag from 0.46 to 0.88 wt% promoted the precipitation of Ω phase, thereby leading to the noticeable improvement on the strength properties of the underaged Al-Cu-Mg alloys at various temperatures. This enhanced precipitation of Ω phase was also accompanied by the suppressed formation of θⲠphase. Despite further exposing at 300 °C lead to a pronounced decrease in the number density of Ω phase, the higher plate number density was still revealed in 0.88Ag alloy rather than 0.46Ag alloy. Moreover, quantitative TEM results of the studied alloys highlighted the differences in the coarsening kinetics of Ω phase during further exposing at 300 °C. Ω phase tended to experience a transition from the plate thickening to the plate lengthening by increasing Ag at 300 °C. Our results also present the positive effect of pre-aging at 165 °C for 2 h on retarding the thickening kinetics of Ω phase at 300 °C.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 611, 12 August 2014, Pages 69-76
Journal: Materials Science and Engineering: A - Volume 611, 12 August 2014, Pages 69-76
نویسندگان
Song Bai, Xuanwei Zhou, Zhiyi Liu, Peng Xia, Meng Liu, Sumin Zeng,