کد مقاله کد نشریه سال انتشار مقاله انگلیسی ترجمه فارسی نسخه تمام متن
7989800 1515947 2018 48 صفحه PDF سفارش دهید دانلود رایگان
عنوان انگلیسی مقاله ISI
Effect of holding time and interlayer's thickness on the crack initiation and propagation and the dissolving behavior of the heat-treated facet WC grains
ترجمه فارسی عنوان
اثر زمان نگهداری و ضخامت لایه بر روی شروع و انتشار ترک و رفتار حل شدن دانه های توخالی دانه گرمایی
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
سفارش ترجمه تخصصی
با تضمین قیمت و کیفیت
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد فلزات و آلیاژها
چکیده انگلیسی
Post welding heat treatment was performed on dissimilar weldments composed of WC-Co to 316 L stainless steel with 1-mm-, 1.5-mm-, and 2-mm-thick Invar interlayers by heating the samples to 1250 °C for 2 h, 8 h, and 16 h respectively. Cracks initiation and propagation were observed in all samples because of the stress relieving after heat treatment. The increase of the interlayer's thickness tends to partially inhibit the initiation and propagation of cracks. When the holding time is 2 h, the sample fractured in the heat affected zone (HAZ). With the increase of holding time (8 h, 16 h), the samples tended to fracture in the fusion zone. The dissolving behavior of prismatic facets estimated by means of high-angle annular dark field (HAADF) microscopy indicated that the shape of WC grains changed to faceted WC grains during the heat treatment, which exhibited abnormal grain growth in the matrix composing of α-Co and γ-(Fe, Ni). In the fusion zone adjacent to the WC-Co, W-M-C carbides skeleton were formed with a character of continuous rods and isolated islands. The islands had lower tungsten and more binders than the rods. By using transmission electron microscopy - energy dispersive spectroscopy (TEM-EDS), it was found that WC grains and WC/Co/WC interface showed strong plastic deformation with obvious elemental diffusion. Moiré fringes inside the WC and in the matrix were confirmed.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: International Journal of Refractory Metals and Hard Materials - Volume 71, February 2018, Pages 45-60
نویسندگان
, , , , ,
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
سفارش ترجمه تخصصی
با تضمین قیمت و کیفیت