Cementites decomposition of a pearlitic ductile cast iron during graphitization annealing heat treatment
ترجمه فارسی عنوان
تجزیه سیمنیتی از یک آهنرنگ پرلید چدنی در طی عملیات حرارتی گرمایی
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
چدن پرلیتی چدنی، تجزیه سیمونیت، نفوذ، اتم کربن، عملیات حرارتی گرم شدن آنیت،
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
چکیده انگلیسی
Cementites decomposition of a pearlitic ductile cast iron during graphitization annealing heat treatment was investigated. Fractographies and microstructures of heat treated samples were observed using a scanning electron microscope and mechanical properties were measured by a universal tensile test machine. The results indicated that during isothermal annealing at 750 °C, the tensile strength of pearlitic ductile cast iron was increased to a peak value at 0.5 h, and decreased gradually thereafter but the elongation was enhanced with the increase of annealing time. Moreover, the diffusion coefficient of carbon atoms could be approximately calculated as 0.56 µm2/s that could be regarded as the shortrange diffusion. As the holding time was short (0. 5 h), diffusion of carbon atoms was incomplete and mainly occurred around the graphites where the morphology of cementites changed from fragmentized shape to granular shape. In addition, the ductile cast iron with tensile strength of 740 MPa and elongation of 7% could be achieved after graphitization annealing heat treatment for 0. 5 h. Two principal factors should be taken into account. First, the decomposition of a small amount of cementites was beneficial for increasing the ductility up to elongation of 7%. Second, the diffusion of carbon atoms from cementites to graphites could improve the binding force between graphites and matrix, enhancing the tensile strength to 740 MPa.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Iron and Steel Research, International - Volume 24, Issue 8, August 2017, Pages 838-843
Journal: Journal of Iron and Steel Research, International - Volume 24, Issue 8, August 2017, Pages 838-843
نویسندگان
Min-qiang Gao, Ying-dong Qu, Guang-long Li, Jun-hua You, Rong-de Li,