Influence of temperature and strain rate on hot deformation behavior of Zr50Ti50 alloy in single β field
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
The deformation behavior and microstructure of the Zr50Ti50 alloy in β phase field were investigated by isothermal compression tests at temperatures ranging from 700 to 850 °C and strain rates ranging from 0.001 to 1 sâ1. The flow curves exhibited typical flow softening. The initial discontinuous yielding behavior was observed at higher strain rates, which was not found in other traditional Zr alloys. The apparent deformation activation energy was calculated to be 103 kJ/mol and constitutive equation describing the flow stress as a function of the strain rate and deformation temperature was proposed. The analysis indicated that the hot deformation mechanism was mainly dominated by dynamic recovery. However, dynamic recrystallization was delayed by dynamic recovery. Thereafter, the processing map was calculated to evaluate the efficiency of the forging process at the temperatures and strain rates investigated and to optimize processing parameters of hot deformation. The optimum processing parameters were found to be 830-850 °C and 0.56-1 sâ1 for hot the deformation of Zr50Ti50 alloy in the β phase region.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Transactions of Nonferrous Metals Society of China - Volume 26, Issue 8, August 2016, Pages 2086-2093
Journal: Transactions of Nonferrous Metals Society of China - Volume 26, Issue 8, August 2016, Pages 2086-2093
نویسندگان
Yun-kai ZHOU, Zhi-hao FENG, Chao-qun XIA, Wen-chang LIU, Qin JING, Shun-xing LIANG, Ming-zhen MA, Zhi-guo ZHANG, Xin-yu ZHANG, Ri-ping LIU,