Fatigue durability and corrosion resistance of TiO2 films on CoCrMo alloy under cyclic deformation
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فناوری نانو (نانو تکنولوژی)
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Smooth and dense TiO2 films with different thickness (45Â nm and 300Â nm respectively) were deposited on a flat CoCrMo substrate by high power impulse magnetron sputtering (HiPIMS). A cantilever resonance method was developed to load cyclic stress on the sheet samples to investigate the fatigue durability of the TiO2 films. The evolution of pre-cracks, which were introduced intentionally in the TiO2 films, was studied at the same time. After cyclic deformation, the corrosion resistance of the TiO2 film coated CoCrMo alloy was investigated by potentiodynamic polarization tests. The results showed that there were no peelings, cracks or delamination of both film types after 1.08Â ÃÂ 107 loading cycles with the maximum stress of 200Â MPa. For the evolution of the pre-cracks in the thicker TiO2 films (300Â nm), new cracks emerged near the pre-cracks in the films, while for the pre-cracks in the thinner TiO2 films (45Â nm) not any new cracks were observed. The thinner films seemed to show better fatigue durability than thicker films. The potentiodynamic polarization tests revealed that the corrosion resistance of the thinner TiO2 films (45Â nm) was not degraded even after 1.08Â ÃÂ 107 loading cycles with the maximum stress of 20Â MPa.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Surface and Coatings Technology - Volume 275, 15 August 2015, Pages 252-259
Journal: Surface and Coatings Technology - Volume 275, 15 August 2015, Pages 252-259
نویسندگان
Dong Xie, Haihua Wang, Rajesh Ganesan, Yongxiang Leng, Hong Sun, Nan Huang,